      PC(聚碳酸酯)EXL4019/沙伯基礎(SABIC)物性表參數

      責任編輯:admin發表時間:2020-06-12 06:30:29

      SABIC(沙伯基礎創新塑料)LEXAN PC EXL4019是不透明的加9%玻璃纖維(GF)增強聚碳酸酯(PC)硅氧烷共聚物樹脂,用于需要提高剛度的注射成型(IM)應用,與常規的GF增強PC樹脂相比,這種樹脂還具有更好的延性,具有介質流動特性和優異的加工性能,與標準PC相比,IM周期更短,LEXAN EXL4019樹脂是一個很好的廣泛的應用,只有有限的顏色可供選擇。
      PC(聚碳酸酯)EXL4019/沙伯基礎(SABIC)物性表參數PDF文檔下載
      PC EXL4019
      以下是PC(聚碳酸酯)EXL4019/沙伯基礎(SABIC)物性表參數
      PROPERTIES   TYPICAL VALUES UNITS TEST METHODS
      MECHANICAL        
      Tensile Stress, yld, Type I, 5 mm/min   55 MPa ASTM D 638
      Tensile Stress, brk, Type I, 5 mm/min   45 MPa ASTM D 638
      Tensile Strain, yld, Type I, 5 mm/min   4.3 % ASTM D 638
      Tensile Strain, brk, Type I, 5 mm/min   14 % ASTM D 638
      Tensile Modulus, 5 mm/min   3950 MPa ASTM D 638
      Flexural Stress, yld, 1.3 mm/min, 50 mm span   103 MPa ASTM D 790
      Flexural Modulus, 1.3 mm/min, 50 mm span   3500 MPa ASTM D 790
      Tensile Stress, yield, 5 mm/min   54 MPa ISO 527
      Tensile Stress, break, 5 mm/min   48 MPa ISO 527
      Tensile Strain, yield, 5 mm/min   4.3 % ISO 527
      Tensile Strain, break, 5 mm/min   8.7 % ISO 527
      Tensile Modulus, 1 mm/min   3900 MPa ISO 527
      Flexural Stress, yield, 2 mm/min   98 MPa ISO 178
      Flexural Modulus, 2 mm/min   3450 MPa ISO 178
      IMPACT        
      Izod Impact, notched, 23°C   345 J/m ASTM D 256
      Izod Impact, notched, -30°C   150 J/m ASTM D 256
      Instrumented Impact Total Energy, 23°C   40 J ASTM D 3763
      Izod Impact, unnotched 80*10*3 +23°C   NB kJ/m² ISO 180/1U
      Izod Impact, unnotched 80*10*3 -30°C   NB kJ/m² ISO 180/1U
      Izod Impact, notched 80*10*3 +23°C   25 kJ/m² ISO 180/1A
      Izod Impact, notched 80*10*3 -30°C   10 kJ/m² ISO 180/1A
      Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm   25 kJ/m² ISO 179/1eA
      Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm   15 kJ/m² ISO 179/1eA
      Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm   NB kJ/m² ISO 179/1eU
      Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm   NB kJ/m² ISO 179/1eU
      THERMAL        
      Vicat Softening Temp, Rate B/50   146 °C ASTM D 1525
      HDT, 1.82 MPa, 3.2mm, unannealed   137 °C ASTM D 648
      CTE, -40°C to 40°C, flow   4.7E-05 1/°C ASTM E 831
      CTE, -40°C to 40°C, xflow   7.E-05 1/°C ASTM E 831
      CTE, -40°C to 40°C, flow   4.7E-05 1/°C ISO 11359-2
      CTE, -40°C to 40°C, xflow   7.E-05 1/°C ISO 11359-2
      Ball Pressure Test, 75°C +/- 2°C   Passes - IEC 60695-10-2
      Vicat Softening Temp, Rate B/50   146 °C ISO 306
      Vicat Softening Temp, Rate B/120   146 °C ISO 306
      HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm   135 °C ISO 75/Ae
      PHYSICAL        
      Specific Gravity   1.25 - ASTM D 792
      Mold Shrinkage, flow, 3.2 mm   0.2-0.6 % SABIC method
      Mold Shrinkage, xflow, 3.2 mm   0.2-0.6 % SABIC method
      Melt Flow Rate, 300°C/1.2 kgf   7.5 g/10 min ASTM D 1238
      Density   1.25 g/cm³ ISO 1183
      Water Absorption, (23°C/saturated)   0.15 % ISO 62-1
      Moisture Absorption (23°C / 50% RH)   0.4 % ISO 62
      Melt Volume Rate, MVR at 300°C/1.2 kg   6 cm³/10 min ISO 1133
      Injection Molding        
      Drying Temperature   120 °C  
      Drying Time   3-4 hrs  
      Drying Time (Cumulative)   48 hrs  
      Maximum Moisture Content   0.02 %  
      Melt Temperature   310-330 °C  
      Nozzle Temperature   305-325 °C  
      Front - Zone 3 Temperature   310-330 °C  
      Middle - Zone 2 Temperature   300-320 °C  
      Rear - Zone 1 Temperature   290-310 °C  
      Mold Temperature   80-115 °C  
      Back Pressure   0.3-0.7 MPa  
      Screw Speed   40-70 rpm  
      Shot to Cylinder Size   40-60 %  
      Vent Depth   0.025-0.076 mm