      當前位置:首頁>>新聞中心>>常見問題

      PC(聚碳酸酯)PC4800/SABIC(沙伯基礎)物性表參數

      責任編輯:admin發表時間:2020-04-20 04:02:58

      沙伯基礎SABIC塑料PC PC4800是一種非常高流動性(MFR = 8.0,250℃/ 1.2kg)聚碳酸酯產品,設計用于光學媒體市場。
      沙伯基礎SABIC塑料PC PC4800物性表參數PDF文檔下載
      PC PC4800
      以下是PC(聚碳酸酯)PC4800/SABIC(沙伯基礎)物性表參數
      PROPERTIES   TYPICAL VALUES UNITS TEST METHODS
      MECHANICAL        
      Tensile Stress, yld, Type I, 50 mm/min   60 MPa ASTM D 638
      Tensile Strain, yld, Type I, 50 mm/min   6 % ASTM D 638
      Tensile Strain, brk, Type I, 50 mm/min   >40 % ASTM D 638
      Tensile Modulus, 50 mm/min   2350 MPa ASTM D 638
      Flexural Stress, yld, 1.3 mm/min, 50 mm span   90 MPa ASTM D 790
      Flexural Modulus, 1.3 mm/min, 50 mm span   2300 MPa ASTM D 790
      Tensile Stress, yield, 50 mm/min   60 MPa ISO 527
      Tensile Strain, yield, 50 mm/min   6 % ISO 527
      Tensile Strain, break, 50 mm/min   >40 % ISO 527
      Tensile Modulus, 1 mm/min   2350 MPa ISO 527
      Flexural Stress, yield, 2 mm/min   90 MPa ISO 178
      Flexural Modulus, 2 mm/min   2300 MPa ISO 178
      IMPACT        
      Izod Impact, unnotched 80*10*3 +23°C   NB kJ/m² ISO 180/1U
      Izod Impact, unnotched 80*10*3 -30°C   NB kJ/m² ISO 180/1U
      Izod Impact, notched 80*10*3 +23°C   15 kJ/m² ISO 180/1A
      Izod Impact, notched 80*10*3 -30°C   12 kJ/m² ISO 180/1A
      THERMAL        
      Vicat Softening Temp, Rate B/50   138 °C ASTM D 1525
      HDT, 0.45 MPa, 3.2 mm   132 °C ASTM D 648
      HDT, 1.82 MPa, 3.2 mm   122 °C ASTM D 648
      CTE, -40°C to 95°C, flow   7.E-05 1/°C ASTM E 831
      Thermal Conductivity   0.2 W/m-°C ASTM C177
      Thermal Conductivity   0.2 W/m-°C ISO 8302
      CTE, 23°C to 80°C, flow   7.E-05 1/°C ISO 11359-2
      Ball Pressure Test, 125°C +/- 2°C   Passes - IEC 60695-10-2
      Vicat Softening Temp, Rate B/50   138 °C ISO 306
      HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm   132 °C ISO 75/Bf
      HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm   122 °C ISO 75/Af
      PHYSICAL        
      Specific Gravity   1.2 - ASTM D 792
      Water Absorption, equilibrium, 23C   0.35 % ASTM D 570
      Mold Shrinkage on Tensile Bar, flow   0.5-0.7 % SABIC method
      Melt Flow Rate, 250°C/1.2 kgf   8 g/10 min ASTM D 1238
      Density   1.2 g/cm³ ISO 1183
      Water Absorption, (23°C/sat)   0.35 % ISO 62
      Melt Volume Rate, MVR at 250°C/1.2 kg   7 cm³/10 min ISO 1133
      OPTICAL        
      Light Transmission, 2.54 mm   >90 % ASTM D 1003
      Haze, 2.54 mm   <0.7 % ASTM D 1003
      Refractive Index   1.586 - ASTM D542
      Refractive Index   1.586 - ISO 489
      ELECTRICAL        
      Volume Resistivity   >1.E+15 Ohm-cm IEC 60093
      Relative Permittivity, 1 MHz   3 - IEC 60250
      Dissipation Factor, 1 MHz   0.01 - IEC 60250
      Injection Molding        
      Drying Temperature   120 °C  
      Drying Time   4-6 hrs  
      Maximum Moisture Content   0.02 %  
      Melt Temperature   340-370 °C  
      Nozzle Temperature   340-370 °C  
      Front - Zone 3 Temperature   350-380 °C  
      Middle - Zone 2 Temperature   320-340 °C  
      Rear - Zone 1 Temperature   270-290 °C  
      Hopper Temperature   60-80 °C  
      Mold Temperature   75-95 °C
      1)僅限典型值。 對于各種顏色,正常公差范圍內的變化是可能的。 在23℃/ 50%相對濕度下儲存至少48小時后測量所有值。 除熔體體積和熔體流動速率外,所有性能均在注塑樣品上測量。 根據ISO 294制備在ISO測試標準下測試的所有樣品。
      2)僅用于選擇目的的典型數據。 不得用于零件或工具設計。
      3)由實驗室試樣制成的測量值。 由于加工條件,設備,零件幾何形狀和工具設計的不同,實際收縮率可能會超出范圍。 建議在切割新模塑制品的工具之前,使用替代或傳統工具進行模具收縮研究。


      溫馨提示:
      本物性表參數提供者不承擔任何法律責任,建議在選擇材料前,就數據值與塑膠材料廠商進行驗證。版權歸原作者所有,如有侵權請立即與我們聯系.