      當前位置:首頁>>新聞中心>>常見問題

      LEXAN(沙伯基礎)3413R/PC(聚碳酸酯)物性表參數

      責任編輯:admin發表時間:2020-04-20 02:50:58

      沙伯基礎SABIC塑料LEXAN 3413R聚碳酸酯(PC)是一種可注射成型的阻燃級產品,填充30%玻璃纖維, 它具有UL94 V1 @ 2mm等級,并提供各種不透明顏色選項。
      沙伯基礎SABIC塑料LEXAN 3413R PC物性表參數PDF文檔下載
      LEXAN 3413R
      以下是LEXAN(沙伯基礎)3413R/PC(聚碳酸酯)物性表參數
      PROPERTIES   TYPICAL VALUES UNITS TEST METHODS
      MECHANICAL        
      Taber Abrasion, CS-17, 1 kg   24 mg/1000cy SABIC method
      Tensile Stress, break, 5 mm/min   100 MPa ISO 527
      Tensile Strain, break, 5 mm/min   2 % ISO 527
      Tensile Modulus, 1 mm/min   9000 MPa ISO 527
      Flexural Stress, break, 2 mm/min   130 MPa ISO 178
      Flexural Modulus, 2 mm/min   7000 MPa ISO 178
      IMPACT        
      Izod Impact, unnotched 80*10*3 +23°C   35 kJ/m² ISO 180/1U
      Izod Impact, unnotched 80*10*3 -30°C   35 kJ/m² ISO 180/1U
      Izod Impact, notched 80*10*3 +23°C   7 kJ/m² ISO 180/1A
      Izod Impact, notched 80*10*3 -30°C   6 kJ/m² ISO 180/1A
      Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm   6 kJ/m² ISO 179/1eA
      Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm   5 kJ/m² ISO 179/1eA
      Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm   40 kJ/m² ISO 179/1eU
      Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm   40 kJ/m² ISO 179/1eU
      THERMAL        
      Thermal Conductivity   0.22 W/m-°C ISO 8302
      CTE, 23°C to 80°C, flow   2.5E-05 1/°C ISO 11359-2
      Ball Pressure Test, 125°C +/- 2°C   PASSES - IEC 60695-10-2
      Vicat Softening Temp, Rate B/50   147 °C ISO 306
      Vicat Softening Temp, Rate B/120   145 °C ISO 306
      HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm   144 °C ISO 75/Be
      HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm   139 °C ISO 75/Ae
      Relative Temp Index, Elec   130 °C UL 746B
      Relative Temp Index, Mech w/impact   125 °C UL 746B
      Relative Temp Index, Mech w/o impact   130 °C UL 746B
      PHYSICAL        
      Mold Shrinkage on Tensile Bar, flow   0.1-0.4 % SABIC method
      Density   1.44 g/cm³ ISO 1183
      Water Absorption, (23°C/sat)   0.26 % ISO 62
      Moisture Absorption (23°C / 50% RH)   0.11 % ISO 62
      Melt Volume Rate, MVR at 300°C/1.2 kg   5 cm³/10 min ISO 1133
      OPTICAL        
      Haze, 2.54 mm   NA % ASTM D 1003
      Refractive Index   NA - ISO 489
      ELECTRICAL        
      Volume Resistivity   >1.E+15 Ohm-cm IEC 60093
      Surface Resistivity, ROA   >1.E+15 Ohm IEC 60093
      Dielectric Strength, in oil, 0.8 mm   33 kV/mm IEC 60243-1
      Dielectric Strength, in oil, 1.6 mm   25 kV/mm IEC 60243-1
      Dielectric Strength, in oil, 3.2 mm   16 kV/mm IEC 60243-1
      Relative Permittivity, 1 MHz   3 - IEC 60250
      Dissipation Factor, 50/60 Hz   0.001 - IEC 60250
      Dissipation Factor, 1 MHz   0.01 - IEC 60250
      Relative Permittivity, 50/60 Hz   3.1 - IEC 60250
      FLAME CHARACTERISTICS        
      UL Recognized, 94V-0 Flame Class Rating   1.5 mm UL 94
      Glow Wire Flammability Index 850°C, passes at   1 mm IEC 60695-2-12
      Glow Wire Flammability Index 960°C, passes at   1.6 mm IEC 60695-2-12
      Oxygen Index (LOI)   38 % ISO 4589
      Injection Molding        
      Drying Temperature   120 °C  
      Drying Time   2-4 hrs  
      Maximum Moisture Content   0.02 %  
      Melt Temperature   290-320 °C  
      Nozzle Temperature   280-310 °C  
      Front - Zone 3 Temperature   290-320 °C  
      Middle - Zone 2 Temperature   280-310 °C  
      Rear - Zone 1 Temperature   270-300 °C  
      Hopper Temperature   60-80 °C  
      Mold Temperature   80-120 °C

      溫馨提示:
      本物性表參數提供者不承擔任何法律責任,建議在選擇材料前,就數據值與塑膠材料廠商進行驗證。版權歸原作者所有,如有侵權請立即與我們聯系.